Product Introduction
Composition Chlorinated rubber as the base material, add plasticizers, pigments, fillers, additives, solvents, and so on.
Agent, solvents, and other components.
Characteristics Excellent weather aging resistance, salt spray resistance, water resistance, alkali corrosion resistance, chemical atmosphere resistance, film tough and wear-resistant.
Resistant to chemical atmosphere, paint film is tough and wear-resistant, strong adhesion to steel, fast drying.
It can be used in low temperature construction, with good matching of bottom and surface, thick slurry type paint chlorinated rubber antirust primer.
Thick film at one time, convenient construction.
It can be widely used in ships, gas cabinets, harbors, wharves, offshore platforms and steel structures.
It can be widely used in the splash zone of ships, gas cabinets, seaports, wharves, steel structures of offshore platforms, the outer walls of petroleum and chemical equipments, chemical pipelines, pipelines, stents,
It can be widely used as anticorrosion of the outer wall of petroleum and chemical equipments, chemical pipelines, pipelines, stents, plants and other steel equipments as well as the outer wall of acid, alkali and salt storage tanks.
Coating method Brushing, rolling and spraying are available.
Diluent Special diluent for chlorinated rubber anticorrosive paint.
Drying time 23±2℃ surface drying ≤ 0.5 hours, drying ≤ 24 hours, fully cured for 7 days.
Painting interval More than 0.5 hours.
Thickness of dry film 30-35 µm/period
Storage period 12 months
Surface treatment The surface of steel should be descaled by hand up to St3 level, and descaled by jet up to Sa2.5 level.
Precautions 1, chlorinated rubber anticorrosive coating should be dried at room temperature for at least 7 days before being put into use.
2、No open-air construction in rain, fog or snow.
Agent, solvents, and other components.
Characteristics Excellent weather aging resistance, salt spray resistance, water resistance, alkali corrosion resistance, chemical atmosphere resistance, film tough and wear-resistant.
Resistant to chemical atmosphere, paint film is tough and wear-resistant, strong adhesion to steel, fast drying.
It can be used in low temperature construction, with good matching of bottom and surface, thick slurry type paint chlorinated rubber antirust primer.
Thick film at one time, convenient construction.
It can be widely used in ships, gas cabinets, harbors, wharves, offshore platforms and steel structures.
It can be widely used in the splash zone of ships, gas cabinets, seaports, wharves, steel structures of offshore platforms, the outer walls of petroleum and chemical equipments, chemical pipelines, pipelines, stents,
It can be widely used as anticorrosion of the outer wall of petroleum and chemical equipments, chemical pipelines, pipelines, stents, plants and other steel equipments as well as the outer wall of acid, alkali and salt storage tanks.
Coating method Brushing, rolling and spraying are available.
Diluent Special diluent for chlorinated rubber anticorrosive paint.
Drying time 23±2℃ surface drying ≤ 0.5 hours, drying ≤ 24 hours, fully cured for 7 days.
Painting interval More than 0.5 hours.
Thickness of dry film 30-35 µm/period
Storage period 12 months
Surface treatment The surface of steel should be descaled by hand up to St3 level, and descaled by jet up to Sa2.5 level.
Precautions 1, chlorinated rubber anticorrosive coating should be dried at room temperature for at least 7 days before being put into use.
2、No open-air construction in rain, fog or snow.