Product Introduction
Composition: Chlorosulphonated polyethylene resin, modified resin as base material, add plasticizer, anti-rust pigment, filler and other materials.
It is composed of chlorosulfonated polyethylene resin, modified resin as base material, plasticizer, anti-rust pigment, filler, solvent, anti-sinking agent and so on.
Characteristics Good antirust property, tough paint film, strong adhesion, fast drying, low temperature construction.
It can be used in metallurgy, metallurgy, metallurgy, metallurgy, and metallurgy.
It can be widely used as chemical pipelines and pipelines in metallurgy, petroleum, chemical industry, construction, seaport, wharf and energy industry.
It can be widely used in metallurgy, petroleum, chemical, construction, seaport, wharf, energy and other industries as chemical pipeline, pipeline, support, plant and other steel structure equipment and facilities.
It can also be used for the anti-corrosion of the outer wall of acid, alkali and salt storage tanks, as well as for the anti-corrosion of concrete structure tower, cement wall, sewage tank, and so on.
It can also be used for concrete structure tower, cement wall, sewage tank and other concrete facilities surface coating.
Coating method Brushing, rolling, spraying can be used.
Diluent Chlorosulfonated polyethylene anticorrosive paint special diluent
Applicable period 23±2℃ 12 hours
Drying time 23±2℃ surface drying ≤ 0.5 hours, drying ≤ 24 hours, fully cured for 7 days.
Storage period 12 months
Chlorosulfonated polyethylene antirust primer, chlorosulfonated polyethylene intermediate paint.
Chlorosulfonated polyethylene topcoat or chlorinated rubber topcoat, etc.
Surface treatment Remove oil and rust, the surface of steel should be descaled manually up to St3 level, and jet descaled up to Sa2.5 level.
Attention 1. Chlorosulphonated polyethylene anticorrosion coating should be dried at room temperature for at least 7 days before it is put into use.
Use
2, rain, fog, snow can not be open construction (humidity ≥ 75%)
It is composed of chlorosulfonated polyethylene resin, modified resin as base material, plasticizer, anti-rust pigment, filler, solvent, anti-sinking agent and so on.
Characteristics Good antirust property, tough paint film, strong adhesion, fast drying, low temperature construction.
It can be used in metallurgy, metallurgy, metallurgy, metallurgy, and metallurgy.
It can be widely used as chemical pipelines and pipelines in metallurgy, petroleum, chemical industry, construction, seaport, wharf and energy industry.
It can be widely used in metallurgy, petroleum, chemical, construction, seaport, wharf, energy and other industries as chemical pipeline, pipeline, support, plant and other steel structure equipment and facilities.
It can also be used for the anti-corrosion of the outer wall of acid, alkali and salt storage tanks, as well as for the anti-corrosion of concrete structure tower, cement wall, sewage tank, and so on.
It can also be used for concrete structure tower, cement wall, sewage tank and other concrete facilities surface coating.
Coating method Brushing, rolling, spraying can be used.
Diluent Chlorosulfonated polyethylene anticorrosive paint special diluent
Applicable period 23±2℃ 12 hours
Drying time 23±2℃ surface drying ≤ 0.5 hours, drying ≤ 24 hours, fully cured for 7 days.
Storage period 12 months
Chlorosulfonated polyethylene antirust primer, chlorosulfonated polyethylene intermediate paint.
Chlorosulfonated polyethylene topcoat or chlorinated rubber topcoat, etc.
Surface treatment Remove oil and rust, the surface of steel should be descaled manually up to St3 level, and jet descaled up to Sa2.5 level.
Attention 1. Chlorosulphonated polyethylene anticorrosion coating should be dried at room temperature for at least 7 days before it is put into use.
Use
2, rain, fog, snow can not be open construction (humidity ≥ 75%)