Composition It is composed of epoxy resin as base material, adding ferruginous iron powder, additives, solvents and polyacylamine ester curing agent.
It is composed of epoxy resin as base material, ferric oxide powder, additives, solvents and polyacrylamide ester curing agent, etc. It is packed in A and B components.
Characteristics Containing a large amount of mica powder in the paint film, it has physical shielding effect, excellent antirust property, good adhesion, resistance to rust.
Excellent, good adhesion, good water resistance, matching zinc-rich primer has excellent resistance to salt spray!
Salt spray resistance!
It can be widely used as antirust intermediate paint for metal structures, ship bottoms, gas storage tanks, bridges, pylons and oil tanks.
It can be widely used as antirust intermediate paint for metal structures, ship bottoms, gas storage tanks, bridges, pylons and oil tanks.
Painting method Brushing, rolling, spraying can be used.
Diluent Special diluent for epoxy anticorrosion paint.
Drying time 23±2℃ surface drying ≤ 0.5 hours, drying ≤ 24 hours, fully cured 7 days
Maturing period 20 minutes can be used
Applicable period 23±2℃ 5 hours
Surface treatment The steel surface should be degreased and descaled, and the manual descaling should be up to St3 level, and the spray descaling should be up to Sa2.5 level.
Precautions 1, epoxy anticorrosive coating should be dried at room temperature for at least 7 days before being put into use.
2, rain, fog, snow can not be open-air construction (humidity ≥ 75% is not recommended for construction)
3. After mixing A and B, it is recommended to use it within 6h!
4. A and B two components must be mixed evenly!