Composition from the epoxy resin as a base material, adding metal zinc powder, additives, solvents, and polyamide ester curing agent and other components.
Amide ester curing agent and other components, divided into A and B two-component packaging.
Characteristics Containing a large amount of zinc powder in the paint film, it has cathodic protection, excellent antirust property, good adhesion, good resistance.
The paint film contains a large amount of zinc powder, with cathodic protection, excellent antirust property, good adhesion, good water resistance and excellent salt spray resistance!
It can be widely used as antirust primer for metal structure, ship bottom, gas storage tanks, bridges, pylons and oil tanks.
It can be widely used as antirust primer for metal structures, ship bottoms, gas storage tanks, bridges, pylons, oil tanks, and is the best primer for epoxy top coat and other
Paint
Painting method Brushing, rolling, spraying are available.
Diluent Special diluent for epoxy anticorrosive paint.
Drying time 23±2℃ surface drying ≤ 0.5 hours, drying ≤ 24 hours, fully cured 7 days.
Applicable period 23±2℃ 5 hours
Surface treatment Steel surface should be degreased and descaled, manual descaling up to Sa3 level, jet descaling up to Sa2.5 level.
Post-coating Epoxy paint, acrylate paint, polyurethane paint, vinyl paint, etc.
Precautions 1, epoxy anticorrosion coating should be dried at room temperature for at least 7 days before being put into use.
2, rain, fog, snow can not be open-air construction (humidity ≥ 75% is not recommended construction)
3. After mixing A and B, it is recommended to use it within 6h!
4. A and B two components must be mixed evenly!