Highly chlorinated polyethylene paint is composed of highly chlorinated polyethylene resin, epoxy resin as base material, plasticizer, filler, solvent, anti-sinking agent and so on.
It is composed of high chlorinated polyethylene resin, epoxy resin as base material, plasticizer, filler, solvent and anti-sinking agent.
Characteristics Good aging resistance, high film hardness, strong adhesion, fast drying.
Excellent chemical resistance, flame retardant, good mechanical properties, can be low temperature construction, bottom
It has good matching property of bottom and surface.
It can be widely used as the surface coating of chemical atmosphere and various steel facilities. Such as bridges, factories, tunnels, steel structures, etc.
Tunnel, steel structure, etc.
Painting method Brushing, rolling and spraying are available.
Diluent Highly chlorinated polyethylene anticorrosive paint special diluent.
Drying time 23±2℃ surface drying ≤2 hours, drying ≤24 hours, fully cured for 7 days.
Painting interval More than 6 hours.
Theoretical dosage 200-220 g/m2 (one time)
Dry film thickness 30-35 µm/repetition
Storage period 12 months
Pre-coating Highly chlorinated polyethylene antirust primer, Highly chlorinated polyethylene intermediate paint.
After coating Highly chlorinated polyethylene top coat or chlorinated rubber top coat, etc.
Surface treatment Degreasing and rust removing, steel surface should be descaled manually up to St3 level, and jet descaled up to Sa2.5 level, and the surface of steel surface should be descaled manually up to Sa2.5 level.
Precautions 1. Highly chlorinated polyethylene anticorrosive coating should be dried under normal temperature for at least 7 days before it is put into use.
Use
3, rain, fog, snow can not be open-air construction (humidity ≥ 75% is not recommended for construction)