It is composed of perchloroethylene resin, modified resin as base material, plasticizer, antirust pigment, filler, auxiliary agent and other materials.
It is composed of perchloroethylene resin, modified resin as base material, plasticizer, antirust pigment, filler, additives, solvent and so on.
Characteristics: Fast drying, strong adhesion, good hardness and flexibility, waterproof and moisture-proof paint film, oil-resistant, acid and alkali corrosion-resistant.
Resistant to oil, acid and alkali corrosion, long-term exposure to the sun, is not easy to chalk, paint film cold, mildew, good insulation.
anti-mold, good insulation
It can be widely used in metallurgy, petrochemical, machinery and other industries for pipeline, steel structure, concrete structure and other facilities.
Painting of facilities.
Painting method Brushing, rolling and spraying are available.
Diluent Special diluent for perchloroethylene anticorrosive paint.
Drying time 23±2℃ surface drying ≤0.5 hours, drying ≤24 hours, fully cured for 7 days.
Painting interval More than 0.5 hours.
Theoretical dosage 200-220 g/m2 (one time)
Dry film thickness 30-35 µm/repetition
Storage period 12 months
Pre-coating Perchloroethylene anticorrosive primer, epoxy primer, chlorinated rubber primer, high chlorinated polyethylene primer.
Post-coating Vinyl chloride anticorrosive topcoat
Surface treatment The surface of steel should be descaled by hand up to St3 grade, and jet descaled up to Sa2.5 grade.
Precautions 1. The perchloroethylene anticorrosive coating should be dried at room temperature for at least 7 days before it is put into use.
2、No open-air construction in rain, fog or snow.